Parcel Orders over $300 Ship Free.
Sika SikaWrap Hex 113C 50inx 300ft Roll 1250sf
SikaWrap Hex-113 C is a bi-directional carbon fiber fabric in a 50 in x 300 ft roll for structural strengthening. It field-laminates with Sikadur epoxy for shear, confinement, and flexural CFRP work on complex shapes.
- Bi-directional carbon fiber fabric, 5.7 oz per sq yd
- Wet or dry lay-up with Sikadur laminating epoxies
- Shear, confinement, and flexural strengthening
SikaWrap Hex-113 C
SikaWrap Hex-113 C is a bi-directional carbon fiber fabric field-laminated with Sikadur 300/Hex 300, Sikadur 301, or Sikadur Hex 330 to form a CFRP strengthening system. This 50 in x 300 ft roll is a lighter bi-directional fabric; for a heavier 0/90 fabric, see SikaWrap Hex-115 C. Area density is 5.7 oz per sq yd with wet or dry lay-up for shear, confinement, and flexural work.
Key Features
- Bi-directional (0/90) carbon fiber fabric
- 5.7 oz per sq yd (196 gsm) area density
- Wet or dry lay-up application
- Used for shear, confinement, or flexural strengthening
- Wraps complex shapes with low aesthetic impact
- Laminates with Sikadur 300/Hex 300, 301, or Hex 330
Applications
- Structural strengthening for load increases
- Seismic column wrapping and masonry walls
- Repair after impact, aging, or fire exposure
- Corrections for insufficient reinforcement or structural depth
Technical Specifications
| Property | Value |
|---|---|
| Manufacturer | Sika |
| Product | SikaWrap Hex-113 C |
| Type | Bi-directional carbon fiber fabric |
| Pack | 50 in x 300 ft roll |
| Fiber type | 0/90 bi-directional carbon |
| Area density | 5.7 oz per sq yd (196 gsm) |
| Nominal ply thickness | 0.010 in design value |
| Design tensile strength | 66,000 psi |
| Design tensile modulus | 6.0 x 10^6 psi |
| MPN | 107711 |
Product documents: SikaWrap Hex-113 C PDS (PDF)
Frequently Asked Questions
What strengthening work is SikaWrap Hex-113 C used for?
Shear, confinement, and flexural strengthening of structural elements. Typical drivers include load increases, seismic upgrades, damage repair, and design corrections.
What fiber construction does SikaWrap Hex-113 C use?
Bi-directional 0/90 carbon fiber at 5.7 oz per sq yd with a 0.010 in design nominal ply thickness.
What epoxy laminates SikaWrap Hex-113 C?
Sikadur 300/Hex 300, Sikadur 301, or Sikadur Hex 330 form the CFRP laminate. Wet and dry lay-up methods are both published.
What design tensile strength does SikaWrap Hex-113 C provide?
Design tensile strength is 66,000 psi by ASTM D3039, or 660 lbs per inch width per layer by ASTM D7565.
What dry-fiber tensile strength does SikaWrap Hex-113 C have?
Published dry fiber tensile strength is 5 x 10^5 psi, with modulus 33.4 x 10^6 psi and elongation at break 1.5%.
What lay-up methods suit SikaWrap Hex-113 C?
Wet or dry lay-up. Dry lay-up places fabric into resin on the substrate; wet lay-up impregnates the fabric before placement.